Rang:
Rang | ISO-waaier | Kobalt % | Dichtheid g/cm3 |
Hardheid HRA |
TRS N/mm2 |
YG8 | K30 | 8 | 14.80 | 89.5 | 2200 |
YG6 | K20 | 6 | 14.95 | 90.5 | 1900 |
YG6X | K10 | 6 | 14.95 | 91.5 | 1800 |
YL10.2 | K30 | 10 | 14.50 | 91.8 | 2400 |
YG13X | K30-K40 | 13 | 14.30 | 89.5 | 2600 |
YG15 | K40 | 15 | 14.00 | 87.5 | 2800 |
Grootte:
D (mm) | Tol (mm) | D (mm) | Tol (mm) | TK (mm) | Tol (mm) | L (mm) | Tol (mm) | A (mm) |
6.3 | 0~+0.3 | 1 | ±0.10 | 3 | -0.2 | 330 | 0~+5.0 | 0,15 |
8.3 | 0~+0.3 | 1 | ±0.15 | 4 | -0.3 | 330 | 0~+5.0 | 0,15 |
10.3 | 0~+0.3 | 1.4 | ±0.15 | 5 | -0.3 | 330 | 0~+5.0 | 0,2 |
12.3 | 0~+0.4 | 1.75 | ±0.15 | 6 | -0.5 | 330 | 0~+5.0 | 0,3 |
14.3 | 0~+0.4 | 1.75 | ±0.15 | 7 | -0.5 | 330 | 0~+5.0 | 0,37 |
16.3 | 0~+0.4 | 2 | ±0.20 | 8 | -0.5 | 330 | 0~+5.0 | 0,4 |
18.3 | 0~+0.5 | 2 | ±0.20 | 9 | -0.8 | 330 | 0~+5.0 | 0,5 |
20.4 | 0~+0.5 | 2.5 | ±0.20 | 10 | -0.8 | 330 | 0~+5.0 | 0,5 |
Wij zijn van het het Wolframcarbide van Zhuzhou Grewin de Hulpmiddelenco., Ltd. De vierkante staaf van het wolframcarbide is een vorm voor vierkant, en het is een soort staaf. Is de vierkante staaf van het wolframcarbide harde, brosse ceramisch die, wanneer gecombineerd met 6% aan 10%-Kobalt, een taai cermet vormt. Dit materiaal werd ontwikkeld voor gebruik in scherpe hulpmiddelen, die harde ceramische kristallen van een paar microns in grootte hebben binnen een kneedbare metaalmatrijs.